ZG-P-8130/ZG-I-8260

ZG-P-8130/ZG-I-8260,Cole Resistance Polyester Pu,Cold Resistance Sole PU Resin in Factory

Cole Resistance Polyester Pu

Cold Resistance Sole PU Resin in Factory

PU Resin for shoe sole of cold-resistant shoes

Characteristic: Medium hardness, medium and low density, cold resistance and semi cold resistance

Application: Applicable to the production of cold-resistant and half hardy soles for both men and women shoes

Typical properties of China Cold Resistance Sole PU Resin

Name of products	Appearance	Viscosity(Pa·s/50℃)	Density(g/cm3/40℃)	Package(kg)
ZG-P-8130	White or pale yellow, liquid, no foreign material	1.00-1.40	1.16-1.20	18
ZG-I-8260	Transparent liquid, no foreign materials	0.20-0.40	1.18-1.20	20

Reference shipments ratio: A/B=30/24(barrel)

Catalysts and auxiliary agents:

ZG-P-8130/ZG-AC-2/water =18kg/220g/0-30g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Reactivity	Technical index	Test item	Reference physical properties
Reference ratioP+C/I	100/80-82	Molded density of sole(g/cm3)	0.45~0.55
Using temperature(℃)	material: 45-50; B material:38-42	Hardness (type A)	45~55
Cream time(s)	7~9	Tensile strength(MPa)	3.5~4.5
Rise time(s)	30~45	Elongation(％)	350~450
Metal mold temperature(℃)	45~55	NBS abrasion resistance (％)	≥10%
Demould time(min)	5.0~7.0	Free foam density(g/cm3)	0.20~0.26
		Folding endurance (room temperature)(40,000 gap length mm)	＜8

China Semi Cold Resistance Sole PU Resin Molding conditions & physical properties:

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.