ZG-P-3650S/ZG-I-9823

ZG-P-3650S/ZG-I-9823,Low Hardness Sole PU Resin Supplier,Low Density Low Hardness Sole Pu

Low Hardness Sole PU Resin Supplier

Low Density Low Hardness Sole Pu

PU Resin for Auto Parts

Characteristic: Medium and low hardness, medium density

Characteristic: Applicable to the production of related auto parts.

Typical properties of PU Resin

Name of products

Appearance

Viscosity(Pa·s/50℃)

Density(g/cm3/40℃)

Package(kg)

ZG-P-3650S

White or pale yellow, liquid, no foreign material

0.50-0.90

1.16-1.20

18

ZG-I-9823

Transparent liquid, no foreign material

0.05-0.20

1.18-1.20

20

Reference shipments ratio: A/B=28/25 (barrel)

Catalysts and auxiliary agents:

ZG-P-3650S/ZG-AC-2/water =18kg/280g/80g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Poly ISO For Shoe Sole Molding conditions & physical properties:

Reactivity

Technical index

Test item

Referencephysical properties

Reference ratioP+C/I

100/87-89

Molded density of sole(g/cm3)

0.35~0.42

Using temperature(℃)

material:45-50;B material:38-42

Hardness (type A)

60~70

Cream time(s)

6~9

Tensile strength(MPa)

3.5~4.5

Rise time(s)

30~45

Elongation(%)

350~450

Metal mold temperature(℃)

45~55

NBS abrasion resistance(%)

≥10%

Demould time(min)

4.0~6.0

Free foam density(g/cm3)

0.24~0.28



mm)Folding endurance (room temperature)(40,000 gap length mm)

<8

Low Hardness Sole PU Resin Supplier

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.

 


bigPhoto
skype Ms. nina

Tel: 86-576-86992777
Mobile: 187 6769 2555
Contact to this supplier

Related Search

Find more related products in following catalogs on Hisupplier.com

Company Info

Zhejiang HengTaiYuan P.U Co., Ltd. [China (Mainland)]


Business Type:Manufacturer
City: Taizhou
Province/State: Zhejiang
Country/Region: China (Mainland)

nina:   skype

You May Like:

Product (16)