ZG-P-6570/ZG-I-5012

ZG-P-6570/ZG-I-5012,Single Density Safety Shoe Sole Pu,Double Density Safety Shoe Sole Pu

Single Density Safety Shoe Sole Pu

Double Density Safety Shoe Sole Pu

Dual density PU Resin for labor protection shoes (safety shoe) sole

Characteristic: Medium and low hardness, medium and high density.

Polyurethane Resin Solution Characteristic: Applicable to the production of single density or double density safety shoes

Typical properties of PU Resin

Name of products	Appearance	Viscosity(Pa·s/50℃)	Density(g/cm3/40℃)	Package(kg)
ZG-P-6570	White or pale yellow, liquid, no foreign material	0.50-0.80	1.16-1.20	18
ZG-I-5012	Transparent liquid, no foreign material	0.20-0.40	1.18-1.20	20

Reference shipments ratio: A/B=30/24 (barrel)

Polyurethane Prepoly For Shoe Sole Catalysts and auxiliary agents:

ZG-P-6570/ZG-AC-2/water=18kg/280g/65~85g/0～800g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Typical processing parameters& Typcal properties:

Reaction characteristics	technical standards	Test item	Physical properties
Reference ratioP+C/I	Outsole: 100/68-70	Molded density(g/cm3)	Outsole: 0.90-1.10
Reference ratioP+C/I	In the base: 100/82-84	Molded density(g/cm3)	In the base: 0.45-0.55
Material temperature(℃)	Amaterial: 45-50; Bmaterial: 38-42	Hardness(type A)	Outsole: 55~75
Material temperature(℃)	Amaterial: 45-50; Bmaterial: 38-42	Hardness(type A)	In the base: 40~55
Cream time(s)	6~9	Tensile strength(MPa)	600~700
End of Rise time(s)	25~35	Elingation(％)	5.0~7.0
Metal mold temperature(℃)	45~55	Wear(％)	≥10%
Demould time(min)	3.0~6.0	Free rise foam density(g/cm3)	Outsole: 0.60~.70
Demould time(min)	3.0~6.0	Free rise foam density(g/cm3)	In the base: 0.28-0.34
		Folding(room temperature)(40,000 gap length mm)	＜8

Low Hardness Sole PU Resin Factory

With the best ratio is based on the ratio, the ratio of value added with The type and quantity of paint additives vary.

The free foam density according to the seasons (temperature, humidity) vary

Ejection time with the increase of the thickness of molded extension

Folding conditions: angle of 90 degrees of flex, frequency of 80 times / min * 4 million

Data listed above are just for reference .The detail data are subjected to practical operation.If other requests for physical properties,please contact us.