ZG-P-8755/ZG-I-7118

ZG-P-8755/ZG-I-7118,High Density Upper Sole PU Resin,White Sole PU Resin

High Density Upper Sole PU Resin

White Sole PU Resin

Q/ZHTY 01—2013

Application: Low hardness, high density.

Characteristic: Suitable for shoes production.

Typical properties of pu resin

Name of products	Appearance	Viscosity(Pa·s/50℃)	Density(g/cm3/40℃)	Packge(kg)
ZG-P-8755	White or pale yellow,liquid foreign material	0.75-0.95	1.16-1.20	18
ZG-I-7118	Tranparent and pure liquid	0.20-0.40	1.18-1.20	20

Reference shipments ratio: A/B=30 / 25(barrel)

Catalysts and auxiliary agents:

ZG-P-8755/ZG-AC-2/water/hardener=18kg/230g/70~90g/300-500g

Endurance High Density Sole PU Resin

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Typical processing parameters& Typcal properties:

Reaction characteristics	technical standards	Test item	Physical properties
Reference ratioP+C/I	100/88-92	Molded density(g/cm3)	0.42-0.50

Material temperature(℃)	A material: 40-45; B material: 38-42	Hardness(type C)	70~80

Cream time(s)	5~8	Tensile strength(kgf/cm)	>10
End of Rise time(s)	25~35	Elingation(％)	350~500
Metal mold temperature(℃)	45~55	DIN	<200
Demould time(min)	3.0~6.0	Free rise foam density(g/cm3)	0.28-0.34

Folding resistance at room temperature	>100000 times	Folding(room temperature)(40,000 gap length mm)	＜8

Sole PU Resin For Shoes Production

With the best ratio is based on the ratio, the ratio of value added with The type and quantity of paint additives vary.

The free foam density according to the seasons (temperature, humidity) vary

Ejection time with the increase of the thickness of molded extension

Folding conditions: angle of 90 degrees of flex, frequency of 80 times / min * 4 million

Data listed above are just for reference. The detail data are subjected to practical operation. If other requests for physical properties, please contact us.