ZG-P-5080/ZG-I-5002

ZG-P-5080/ZG-I-5002,High Density High Hardness Sole Pu,Low-Hardness Shoe Sole PU Resin

High Density High Hardness Sole Pu

Low-Hardness Shoe Sole PU Resin

Q/ZHTY 01—2013

Application: High hardness, high density.

Characteristic: Suitable for female high-heeled shoes production

Typical properties of pu resin

Name of products

Appearance

Viscosity(Pa·s/50℃)

Density(g/cm3/40℃)

Packge(kg)

ZG-P-5080

White or pale yellow,liquid foreign material

0.40-0.80

1.16-1.20

18

ZG-I-5002

Tranparent and pure liquid

0.10-0.30

1.18-1.20

20

Reference shipments ratio: A/B=27/26(barrel)

Sole PU Resin For Business Shoes Catalysts and auxiliary agents

ZG-P-5080/ZG-AC-2/water =18kg/220g/40-80g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Typical processing parameters& Typcal properties

Reaction characteristics

technical standards

Test item

Physical properties

Reference ratioP+C/I

100/106-108

Molded density(g/cm3)

0.42~0.52

Material temperature(℃)

A material
:45-50; B material:38-42

Hardness(type A)

45~60

Cream time(s)

6~9

Tensile strength(MPa)

3.5~5.5

End of Rise time(s)

30~45

Elingation(%)

250~350

Metal mold temperature(℃)

45~55

NBS abrasion resistance

(%)

≥10%

Demould time(min)

5.0~7.0

Free rise foam density(g/cm3)

0.23~0.28



Folding(room temperature)(40,000 gap length mm)

<8

Isocyanate Prepolymer

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.


bigPhoto
skype Ms. nina

Tel: 86-576-86992777
Mobile: 187 6769 2555
Contact to this supplier

Related Search

Find more related products in following catalogs on Hisupplier.com

Company Info

Zhejiang HengTaiYuan P.U Co., Ltd. [China (Mainland)]


Business Type:Manufacturer
City: Taizhou
Province/State: Zhejiang
Country/Region: China (Mainland)

nina:   skype

You May Like:

Product (16)