ZG-P-6687/ZG-I-5002

ZG-P-6687/ZG-I-5002,Children Shoes Sole PU Resin Manufacturer,PU Resin For Men Casual Shoes

Children Shoes Sole PU Resin Manufacturer

PU Resin For Men Casual Shoes

Q/ZHTY 01—2010

Characteristic: High hardness, medium and high density good resilience

Application: Applicable to the production of low-speed type

Typical properties of PU Resin

Name of products	Appearance	Viscosity(Pa·s/50℃)	Density(g/cm3/40℃)	Package(kg)
ZG-P-6687	Milky,liquid, no foreign materia	6.0±2.0	----	18
ZG-I-5002	Transparentliquid, no foreignmaterial	1.5±0.5	----	20

Catalysts and auxiliary agents

ZG-P-6687/ZG-AC-2/water =18kg/220-320g/30-60g/

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Molding conditions & physical properties

Reactivity	Technical index	Test item	Reference physicalproperties
Reference ratioP+C/I	100/110~112	Molded density of sole(g/cm3)	0.5-0.7
Material temperature(℃)	material:45-50 B material:38-42	Hardness (type C)	80~90
Cream time(s)	6~9	Tensile strength(MPa)	3.5~4.5
Rise time(s)		Elongation(％)	250~350
Metal mold temperature(℃)	50~60	NBS abrasion resistance(％)
Demould time(min)	3.0~7.0	Free foam density(g/cm3)	0.30-0.40

Sports Shoes Sole PU Resin

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.