ZG-P-5005/ZG-I-5320

ZG-P-5005/ZG-I-5320,China Medium Hardness Sole PU Resin,Children Shoes Sole PU Resin

China Medium Hardness Sole PU Resin

Children Shoes Sole PU Resin

Medium and high-density PU Resin for shoe sole with the upper

Characteristic: Medium and low hardness, medium and high density

Application: Applicable to the production of shoe sole with the upper for men and women

Typical properties of PU Resin

Name of products	Appearance	Viscosity(Pa·s/50℃)	Density(g/cm3/40℃)	Package(kg)
ZG-P-5005	White or paleyellow, liquid, no foreign material	0.50-0.80	1.16-1.20	18
ZG-I-5320	Transparent liquid, no foreignmaterial	0.20-0.40	1.18-1.20	20

Reference shipments ratio: A/B=30/25 (barrel)

Catalysts and auxiliary agents:

ZG-P-5005/ZG-AC-2/water=18kg/235g/0-40g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

High Resilience Insole PU Resin Factory Molding conditions & physical properties:

Reactivity	Technical index	Test item	Reference physical properties
Reference ratio P+C/I	100/83-85	Molded density of sole(g/cm3)	0.45~0.55
Material temperature(℃)	A material: 45-50; B material:38-42	Hardness (type A)	40~50
Cream time(s)	7~9	Tensile strength(MPa)	6.0~8.0
Rise time(s)	30~45	Elongation(％)	350~450
Metal mold temperature(℃)	45~55	NBS abrasion resistance(％)	≥10%
Demould time(min)	3.0~5.0	Free foam density(g/cm3)	0.25~0.30
		Folding endurance(room temperature) (40,000 gap length mm)	＜8

Low Density Insole PU Resin Supplier

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.