ZG-P-420/ZG-I-218

ZG-P-420/ZG-I-218,PU Resin For Shoe Sole,Medium Hardness Sole PU Resin Factory,low PU Resin for insole

PU Resin For Shoe Sole

Medium Hardness Sole PU Resin Factory

low PU Resin for insole

Characteristic: High resilience, low density

Application: Applicable to the production of insole for sports shoes and leather shoes.

Typical properties of PU Resin

Name of products	Appearance	Viscosity(Pa·s/50℃)	Density(g/cm3/40℃)	Package(kg)
ZG-P-420	White or pale yellow, liquid, no foreign material	0.80-1.40	1.16-1.20	18
ZG-I-218	Transparent liquid, no foreign material	0.10-0.30	1.18-1.20	20

Reference shipments ratio: A/B=31/22 (barrel)

Medium Hardness Sole PU Resin Catalysts and auxiliary agents:

ZG-P-420/ZG-AC-2/water =18kg/220g/80g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Molding conditions & physical properties:

Reactivity	Technical index	Test item	Reference physical properties
Reference ratioP+C/I	100/46-50	Molded density of sole(g/cm3)	0.22~0.30
Material temperature(℃)	material: 35-42; B material:38-42	Hardness (type A)	20~40
Cream time(s)	6~9	Tensile strength(MPa)	6.0~8.0
Rise time(s)	30~45	Elongation(％)	350~450
Metal mold temperature(℃)	45~55	NBS abrasion resistance(％)	≥10%
Demould time(min)	1.5~3.0	Free foam density(g/cm3)	0.10~0.14
		Folding endurance (room temperature)(40,000 gap length mm)	＜8

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.