ZG-P-8086/ZG-I-9823,Low Density High Hardness Sole Pu,Super-High Hardness Shoe Sole PU Resin
Low Density High Hardness Sole Pu
Super-High Hardness Shoe Sole PU Resin
Super high-hardness and super low-density PU Resin for shoe sole
Characteristic: Super-high hardness, super-low density.
Application: Applicable to the production of shoe soles for both men and women
Typical properties of PU Resin
Name of products
Appearance
Viscosity(Pa·s/50℃)
Density(g/cm3/40℃)
Package(kg)
ZG-P-8086
White or pale yellow, liquid, no foreign material
0.30-0.70
1.16-1.20
18
ZG-I-9823
Transparent liquid, no foreign material
0.05-0.20
1.18-1.20
20
Reference shipments ratio: A/B=28/25(barrel)
Catalysts and auxiliary agents
ZG-P-8086/ZG-AC-2/water =18kg/230g/70-120g
Super-Low Density Shoe Sole PU Resin
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties:
Reactivity
Technical index
Test item
Reference physical properties
Reference ratioP+C/I
100/98-102
Molded density of sole(g/cm3)
0.30~0.40
Using temperature(℃)
material: 45-50; B material: 38-42
Hardness (type A)
75~80
Cream time(s)
6~9
Tensile strength(MPa)
—
Rise time(s)
30~45
Elongation(%)
—
Metal mold temperature(℃)
55~65
NBS abrasion resistance(%)
≥10%
Demould time(min)
5.0~7.0
Free foam density(g/cm3)
0.12~0.15
Folding endurance (room temperature)(40,000 gap length mm)
—
PU Prepolymer
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.